Simplified creation of polyester fabric supported Fe-based MOFs by an industrialized dyeing process: Conditions optimization, photocatalytics activity and polyvinyl alcohol removal.

MIL-53(Fe) was successfully prepared and deposited on the surface carboxylated polyester (PET) fiber by an optimized conventional solvothermal or industrialized high temperature pressure exhaustion (HTPE) process to develop a PET fiber supported MIL-53(Fe) photocatalyst (MIL-Fe@PET) for the degradation of polyvinyl alcohol (PVA) in water under light emitting diode (LED) visible irradiation. On the basis of several characterizations, MIL-Fe@PET was tested for the photocalytic ability and degradation mechanism. It was found that temperature elevation significantly enhanced the formation and deposition of MIL-53(Fe) with better photocatalytic activity. However, higher temperature than 130°C was not in favor of its photocatalytic activity. Increasing the number of surface carboxyl groups of the modified PET fiber could cause a liner improvement in MIL-53(Fe) loading content and photocatalytic ability. High visible irradiation intensity also dramatically increased photocatalytic ability and PVA degradation efficiency of MIL-Fe@PET. Na2S2O8 was used to replace H2O2 as electron acceptor for further promoting PVA degradation in this system. MIL-Fe@PET prepared by HTPE process showed higher MIL-53(Fe) loading content and slightly lower PVA degradation efficiency than that prepared by solvothermal process at the same conditions. These findings provided a practical strategy for the large-scale production of the supported MIL-53(Fe) as a photocatalyst in the future.

Activation of Na2S2O8 for dye degradation by Fe complexes fixed on polycarboxylic acids modified waste cotton.

Three aliphatic polycarboxylic acids (PCAs) including tartaric acid (TA), citric acid (CA) and 1,2,3,4-butanetetracarboxylic acid (BTCA) were used for the surface modification of waste cotton fiber by an industrialized pad-dry-cure process to introduce carboxyl groups, which then coordinated with Fe3+ ions to obtain three PCA modified cotton fiber Fe complexes. TA modified cotton fiber could easily react with Fe3+ ions to form its complex with high Fe content. Furthermore, TA modified cotton fiber Fe complex showed a better enhanced effect of activated Na2S2O8 to produce free oxygen radicals for the degradation of an azo dye, Reactive Red 195 than the other two complexes. Different critical Fe contents were found for three complexes to obtain the best enhanced effect.

Safety Profile of TiO2-Based Photocatalytic Nanofabrics for Indoor Formaldehyde Degradation.

Anatase TiO2 nanoparticles (TNPs) are synthesized using the sol-gel method and loaded onto the surface of polyester-cotton (65/35) fabrics. The nanofabrics degrade formaldehyde at an efficiency of 77% in eight hours with visible light irradiation or 97% with UV light. The loaded TNPs display very little release from nanofabrics (~0.0%) during a standard fastness to rubbing test. Assuming TNPs may fall off nanofabrics during their life cycles, we also examine the possible toxicity of TNPs to human cells. We found that up to a concentration of 220 µg/mL, they do not affect viability of human acute monocytic leukemia cell line THP-1 macrophages and human liver and kidney cells.

Heterogeneous fenton degradation of azo dyes catalyzed by modified polyacrylonitrile fiber fe complexes: QSPR (quantitative structure peorperty relationship) study.

The amidoximated polyacrylonitrile (PAN) fiber Fe complexes were prepared and used as the heterogeneous Fenton catalysts for the degradation of 28 anionic water soluble azo dyes in water under visible irradiation. The multiple linear regression (MLR) method was employed to develop the quantitative structure property relationship (QSPR) model equations for the decoloration and mineralization of azo dyes. Moreover, the predictive ability of the QSPR model equations was assessed using Leave-one-out (LOO) and cross-validation (CV) methods. Additionally, the effect of Fe content of catalyst and the sodium chloride in water on QSPR model equations were also investigated. The results indicated that the heterogeneous photo-Fenton degradation of the azo dyes with different structures was conducted in the presence of the amidoximated PAN fiber Fe complex. The QSPR model equations for the dye decoloration and mineralization were successfully developed using MLR technique. MW/S (molecular weight divided by the number of sulphonate groups) and NN=N (the number of azo linkage) are considered as the most important determining factor for the dye degradation and mineralization, and there is a significant negative correlation between MW/S or NN=N and degradation percentage or total organic carbon (TOC) removal. Moreover, LOO and CV analysis suggested that the obtained QSPR model equations have the better prediction ability. The variation in Fe content of catalyst and the addition of sodium chloride did not alter the nature of the QSPR model equations.

Copper-iron bimetal modified PAN fiber complexes as novel heterogeneous Fenton catalysts for degradation of organic dye under visible light irradiation.

A series of Cu-Fe bimetal amidoximated polyacrylonitrile (PAN) fiber complexes with different molar ratios of Cu(2+) to Fe(3+) ions was prepared using a simple exhaustion method, and characterized using FTIR, DRS and XPS, respectively. Then they were tested as the heterogeneous Fenton catalysts for Rhodamine B degradation with H(2)O(2) in the dark and under visible light irradiation. The results indicated that Cu-Fe bimetal amidoximated PAN fiber complexes could more effectively catalyze the dye degradation in water than Fe amidoximated PAN fiber complex, especially in the dark. And introduction of Cu(2+) ions significantly increased their catalytic performance. 0.56 was the optimum molar ratio of Cu(2+) to Fe(3+) ions to achieve the best catalytic activity and stability. This was mainly due to the synergetic effect in the bimetal complexes. Visible light irradiation improved the catalytic activity of the complexes, especially with a low molar ratio of Cu(2+) to Fe(3+) ions.

Preparation and photocatalytic performance of Fe (III)-amidoximated PAN fiber complex for oxidative degradation of azo dye under visible light irradiation.

Polyacrylonitrile (PAN) fiber was modified with hydroxylamine hydrochloride to introduce amidoxime groups onto the fiber surface. These amidoxime groups were used to react with Fe (III) ions to prepare Fe (III)-amidoximated PAN fiber complex, which was characterized using SEM, XRD, FTIR, XPS, DMA, and DRS respectively. Then the photocatalytic activity of Fe-AO-PAN was evaluated in the degradation of a typical azo dye, C. I. Reactive Red 195 in the presence of H(2)O(2) under visible light irradiation. Moreover, the effect of the Fe content of Fe-AO-PAN on dye degradation was also investigated. The results indicated that Fe (III) ions can crosslink between the modified PAN fiber chains by the coordination of Fe (III) ions with the amino nitrogen atoms and hydroxyl oxygen atoms of the amidoximation groups to form Fe (III)-amidoximated PAN fiber complex, and the Fe content of which is mainly determined by Fe (III) ions and amidoximation groups. Fe (III)-amidoximated PAN fiber complex is found to be activated in the visible light region. Moreover, Fe (III)-amidoximated PAN fiber complex shows the catalytic activity for dye degradation by H(2)O(2) at pH=6.0 in the dark, and can be significantly enhanced by increasing light irradiation and Fe content, therefore, it can be used as a new heterogeneous Fenton photocatalyst for the effective decomposition of the dye in water. In addition, ESR spectra confirm that Fe (III)-amidoximated PAN fiber complex can generate more OH radicals from H(2)O(2) under visible light irradiation, leading to dye degradation. A possible mechanism of photocatalysis is proposed.